Re: Soldering

Postby crazypotter » Wed Jul 18, 2018 10:43 am

Thanks to everyone for the advice. Whilst on the subject, and not being au fait with soldering what exactly does "tinning" entail?. What is the best iron and solder to purchase with a tight budget?. Thanks again for the response.

User avatar
Posts: 3588
Joined: Sun Jan 12, 2014 9:58 pm
Location: At the end....... and sometimes at the other end

Re: Soldering

Postby End2end » Wed Jul 18, 2018 11:10 am

"Tinning" is the process of simply melting solder onto something covering it.
You should "Tin" both items that will be soldered together. This helps the solder flow arcross both items when soldering them together.

Another tip from me (as I was soldering last night)
Have a wet sponge handy so you can wipe the excess solder off the end of the soldering iron. DO NOT hold the sponge. Lay it on something and wipe across it.

I cannot comment on cheap soldering irons sadly as I use proper WELLER (£150).
Don't buy UNLEADED / Lead-Free solder. At worst buy a 60/40 mixed solder.
Hope it helps. :)
"St Blazey's" - The progress and predicaments.
St. Blazey's Works & Depot thread

Posts: 41
Joined: Tue Nov 28, 2017 10:15 pm

Re: Soldering

Postby crazypotter » Wed Jul 18, 2018 11:26 am

Thanks for that. If you have say a layout plan with three loops and sidings would you solder one piece of track in each loop and siding or a more random approach?.

Posts: 4656
Joined: Sat Apr 15, 2006 5:48 pm
Location: North Worcs

Re: Soldering

Postby b308 » Wed Jul 18, 2018 11:26 am

For soldering wire to rail using flux cored solder works just fine, also I don't feel whether it is lead or not makes that much difference for this sort of use... I just use what is to hand. Same again for soldering irons, I use Antex irons (£15/25 each) and they work just fine, you don't need to spend a fortune on them, Weller do similar irons in the same price range. Even the cheapo £5 ones will do this sort of work as long as you make sure the parts to be soldered together are properly prepared, i.e. clean and tinned. It's not rocket science, though it's one of those things that you get better at with practice.

I accept that for intricate work then decent tools are a must but for this purpose I don't believe they are a necessity, I've been soldering wires to rails for 40+ years with cheap-ish (i.e. £15) irons and have had no issues... Once you start using them for other purposes then it may be worth investing in a decent variable temperature soldering workstation which is what i assume E2E is referring to...

Totally agree about the sponge, if you get one of those soldering iron stands they come with a place for the sponge...


User avatar
Posts: 3219
Joined: Thu Oct 18, 2007 1:07 pm
Location: SE United Kingdom

Re: Soldering

Postby Flashbang » Wed Jul 18, 2018 11:33 am

Here's my guide to successful soldering. I stands the test of time and if followed works every time!

As this question gets asked many times, I though I'd put a posting on the forum explaining the technique that I was trained to use and have been using for around 50 or so years now!

The basics of soldering are:- A soldering iron of suitable wattage size and tip for the work being undertaken fitted with a clean bit that’s in first class condition, 60/40 lead content Rosin cored solder and clean connections. Lets make a start…. For everyday soldering a minimum 25 watt iron with a small to medium sized bit is required. Larger bit sized irons have their place, but are not always needed for most electrical joints. Larger wattage irons are equally fine to use if the irons tip is of a suitable size. A larger wattage iron is often more desirable as the heat transfer into the item being soldered will be much quicker.

To make a good quality soldered joint, heat the iron for at least five minutes. Don’t rush, the irons tip must be up to full temperature. Have to hand a damp soldering iron's tip cleaning sponge pad. If you own a soldering iron stand its likely it came with a sponge. If not, then cut a piece of ordinary non synthetic sponge and use that. Remember to keep the sponge damp.
Once the iron is hot, wipe the tip onto the sponge to remove all previous oxidisation and old solder residue. Assuming the tip is in a good condition and it must be! Apply a little of the rosin cored solder to the tip.

On electrical joints never use solid stick type solder nor most paste or liquid types of flux, as these all contain a mild acid which over a long period of time causes high resistance problems within the soldered joint. Solid solders and liquid fluxes are normally the reserve of the solid sheet metal soldering jobs – Loco building, plumbing etc.
If you must use flux for electrical joints in addition to what is inbuilt in the rosin cored solder, then ONLY EVER use a special flux designed for electrical soldered joints. It does not contain any harmful acids that would need washing away with water. Examples are:- Carrs Orange label, DCC Concepts Sapphire flux or fluxes sold under the Reflow banner.

For jointing two or more wires together….With the irons tip coated in liquid solder (wetted) and having previously dry assembled the joint - It must be cleaned too, use a fibre glass pencil or scrape the surfaces of both components clean, unless its freshly stripped wire where the sheathing keeps the surface of the wire nice and clean. Place the wetted irons tip directly onto the connection. Wait a few seconds for the heat of the tip to transfer into the wires and then apply a little more rosin corded solder onto the heated joint, not onto the irons tip. You should see the solder start to melt and flow into and around the joint. Once sufficient solder has been applied to coat the whole joint remove both the iron and corded solder. NOW DO NOT TOUCH or MOVE the joint. Wait at least 10 seconds after removing the heat to allow the joint to cool and the solder to set. What you should end up with is a solid, clean joint. Sometimes the PVC sheath on the wire/s being soldered will shrink back a little. This is a nuisance at times and is due to a) The wires PVC sheathing having a low temperature range or b) Too much heat applied to the joint for too long a period of time.

Finally, before you go onto solder another joint or you have completely finished and before you disconnect the iron, clean the tip again on the damp sponge. You will get a many years of use from a soldering iron if you keep its tip clean!

Soldering wires to the bottom or outside of the rail is the same principle, but here I find pre tinning both the end of the wire and the pre cleaned place on the rail where the wire is to connect to be the best method. Pre clean the rail with the aid of a fibre pencil or other means - file or scraper etc. Tin rail with a little solder, both the place on the rail and the wires end. To Tin, apply a small amount of solder to the clean irons tip, then touch the iron onto the area to be tinned. Heat/Solder will flow from the tip onto the area. This should only take a few seconds, keep the irons tip in place and feed some of the cored solder into the area. Remove iron and wipe the tip on the damp sponge. Once every item has been tinned e.g. rail and bared wire end, place the stripped wire end, which if necessary has been pre bent to a small ‘L’ shape, up to the solder on the rail. Apply a little solder to the irons tip and place the iron on top of the wire and lightly press down towards the rail. The hot solder on the irons tip will cause both the wires solder and the rails solder to melt into one. If necessary apply a little more cored solder onto the wire with the iron still in place should there not be enough on the rail to make a solid connection. Carefully remove the iron and ensure the wire maintains in contact with the rail and doesn’t move, waiting for 5 to 10 seconds to allow the soldered joint to cool. The use of a small screwdriver blade or even tweezers to hold the wire in place until the solder solidifies and prevent your fingers burning is an option I often use.

The use of crocodile clips or any similar sprung clamps fixed onto the rails just either side of the soldering work area are advisable, as these act as ‘mini heat shunts’ and help prevent the rail being overheated away from the soldering area which can, if the heat is allowed to be transmitted along the rail, subsequently causing the plastic sleeper fixings to melt.

Don’t forget to wipe the tip on the damp sponge after finishing all the work and before turning off the iron.

One thing that I have found for the beginner to soldering, is to obtain a spare scrap piece of track and some pieces of wire and practise, practice and practice until you feel comfortable and at ease with soldering.
Broken? It was working correctly when I left it.

Posts: 41
Joined: Tue Nov 28, 2017 10:15 pm

Re: Soldering

Postby crazypotter » Wed Jul 18, 2018 2:57 pm

Thanks for that flashbang. Very concise and instructive. Seems I need to bite the bullet and have a bit of practice.

Posts: 679
Joined: Fri Apr 19, 2013 4:25 pm
Location: Sat looking at the computer screen

Re: Soldering

Postby mahoganydog » Wed Jul 18, 2018 3:51 pm

Hi Crazypotter,

in terms of what iron I would recommend the Antex XS25 (they do one with a silicone mains lead so very flexible, try and get this one if you can) which comes with a 3.2mm tip which is fine for everything apart from delicate work like circuit boards and LED's. For these a 2.3mm tip is best (Antex do a full range of accessories and spares) not even a five second job to change the tip; slide one off and the alternative on.

In terms of sourcing I strongly recommend Rapid ( ) for their high speed service and free postage on orders over £30+vat. They do all manner of stands, solder dispensers and wire as well. Remember to click on the "inc VAT" checkbox on the upper right of the page though!

Re Flashbang's mention of scrap track; this has a use other than practicing on. I use a truly mangy bit for holding the fishplates while I solder them. If you can get the wire onto the back of a fishplate it is so much neater than the side of a rail and, once the ballasting is done, invisible.

Good luck

In a world of fences and doors who needs windows and gates?